Carmen Rosso
Hardness (Mohs) 3 - 3,5
Apparent Density (kg / m³) 2,707 ± 0,001
Real Density (kg / m³) 2,708 ± 0,0009
Porosity (%) 0,0658 ± 0,013
Water Absorption (%) 0,024 ± 0,004
Carmen Rosso Queen
Hardness (Mohs) 3 - 3,5
Apparent Density (kg / m³) 2,707 ± 0,001
Real Density (kg / m³) 2,708 ± 0,0009
Porosity (%) 0,0658 ± 0,013
Water Absorption (%) 0,024 ± 0,004
Yenice Fossil Beige
Apparent Density (kg / m³) 2,701 ± 0,002
Real Density (kg / m³) 2,719 ± 0,003
Open Porosity (%) 0,103 ± 0,034
Total Porosity (%) 0,658 ± 0,030
Water Absorption at Atmospheric Pressure 0,038 ± 0,013
Weight Lost After Freezing (%) 0,020 ± 0,003
Hardness (Mohs) 3 - 3,5
Uniaxial Compressive Strength (MPa) 113,76 ± 11,35
Uniaxial Compressive Strength After Freezing and Thawing (MPa)
113,54 ± 3,99
Flexural Strength Under Concentrated (MPa) 11,21 ± 1,46
Bohme Surface Abrassion Values (cm³ / 50 cm²) 8,27 ± 1,37
Large Disk Abrassion (mm) 17,95 ± 0,90
Impact Strength (MPa) 1,73 ± 0,41
Yenice Light Beige
Apparent Density (kg / m³) 2,701 ± 0,002
Real Density (kg / m³) 2,719 ± 0,003
Open Porosity (%) 0,103 ± 0,034
Total Porosity (%) 0,658 ± 0,030
Water Absorption at Atmospheric Pressure 0,038 ± 0,013
Weight Lost After Freezing (%) 0,020 ± 0,003
Hardness (Mohs) 3 - 3,5
Uniaxial Compressive Strength (MPa) 113,76 ± 11,35
Uniaxial Compressive Strength After Freezing and Thawing (MPa)
113,54 ± 3,99
Flexural Strength Under Concentrated (MPa) 11,21 ± 1,46
Bohme Surface Abrassion Values (cm³ / 50 cm²) 8,27 ± 1,37
Large Disk Abrassion (mm) 17,95 ± 0,90
Impact Strength (MPa) 1,73 ± 0,41
Saruhanlı Beige
Saruhan Beige Fiorito

Saruhan Beige Giallo

Saruhan Beige Leopard

Saruhan Beige Rosa

Apparent Density (kg / m³) 2,700 ± 0,003
Real Density (kg / m³) 2,707 ± 0,007
Open Porosity (%) 0,249 ± 0,087
Total Porosity (%) 0,411 ± 0,020
Water Absorption at Atmospheric Pressure 0,092 ± 0,032
Weight Lost After Freezing (%) 0,018 ± 0,009
Hardness (Mohs) 3 - 3,5
Uniaxial Compressive Strength (MPa) 151,99 ± 20,63
Flexural Strength Under Concentrated (MPa) 11,61 ± 2,12
Uniaxial Compressive Strength After Freezing and Thawing (MPa)
11,80 ± 1,98
Bohme Surface Abrassion Values (mm³) 11483 ± 2239
Large Disk Abrassion (mm) 19,90 ± 0,50
Impact Strength (MPa) 1,33 ± 0,33
|
|
|